氟碳喷涂工艺流程
Technological flow of fluorine-carbon spray-painting
钣金加工工艺与设备
Metal sheet processing techniques and equipment
产品介绍 About Products
氟碳铝单板
FlUORINE-CARBON AlUMINUM SINGLE SHEET
氟碳树脂涂料
PVDF
蜂窝板
HONEYCOMB BOARD
邮箱登陆 Mail
用户名:
密  码:
       
当前位置:首页工艺设备喷涂工艺与设备
氟碳喷涂工艺流程Technological flow of fluorine-carbon spray-painting
上 件
Mounting of components
喷底漆
To spray bottom paint
干膜厚度:5-8μm.
Thickness of dry film:5-8μm
流 平
Fluid flatness
室温,环境干净:10min
Indoor temperature, clean environment,10min
喷面漆
To spray surface
干膜厚度:20-25μm.
20-25μm paint thickness of dry film
流 平
Fluid flatness
室温,环境干净:10min
Indoor temperature, clean environment,10min
喷罩光漆
To spray cover paint
喷罩光漆:干膜厚度:10min
To spray cover paint :thickness of dry film:10min
流 平
Fluid flatness
室温,环境干净:10min
Indoor temperature, clean environment,10min
固化烘干
Solidifying and drying
固化烘干:240℃±10℃,20min
Solidifying and drying: 240℃±10℃,20min
自 然
Nature
自然冷却:铝板表面降温至室温
Natural cooling: surface of aluminum sheet lowers to indoor temperature
冷 却
Cooling
检验:膜厚、色差、表面质量
Inspection: thickness of film, chromatic aberration, surface quality